Aluminum Anodization
Application ID: 49061
When anodizing aluminum, the surface is electrochemically altered to form an abrasive and corrosion-resistive Al2O3 film. The electrode kinetics during the process are only marginally affected as the oxide layer grows, so a stationary analysis of the current distribution is sufficient to determine the uniformity of this layer’s thickness.
Anode kinetics from experimental polarization data are used to investigate the uniformity of the anodization current density at three different temperatures, for a specified average current density. At higher temperatures, the cell potential is reduced while the current distribution and thickness become less uniform. This is attributed to lower activation losses (faster kinetics) at higher temperatures.
この model の例は, 通常次の製品を使用して構築されるこのタイプのアプリケーションを示しています.
ただし, これを完全に定義およびモデル化するには, 追加の製品が必要になる場合があります. さらに, この例は, 次の製品の組み合わせのコンポーネントを使用して定義およびモデル化することもできます.
- COMSOL Multiphysics® and
- either the バッテリデザインモジュール, 腐食解析モジュール, 電気化学モジュール, 電気めっきモジュール, or 燃料電池&電解槽モジュール
アプリケーションのモデリングに必要な COMSOL® 製品の組み合わせは, 境界条件, 材料特性, フィジックスインターフェース, パーツライブラリなど, いくつかの要因によって異なります. 特定の機能が複数の製品に共通している場合もあります. お客様のモデリングニーズに適した製品の組み合わせを決定するために, 製品仕様一覧 を確認し, 無償のトライアルライセンスをご利用ください. COMSOL セールスおよびサポートチームでは, この件に関するご質問にお答えしています.